·搪玻璃反应釜技术规范

2、搪瓷反应釜

7、耐冲击性:玻璃层的实验室反应釜内应力越小,弹性越好,硬度越大,抗弯抗压强度越高,则耐冲击就越好。我厂之玻璃层在规定厚度内,用直径30mm,重量112g钢球冲击时,其冲击功为282×10-3J(优等品指标为260×10-3J)。

1, glass lining lab using reactor pressure: 0.2-0.8 Mpa2, lab reaction kettle acid: for a variety of organic acid, inorganic acid, organic solvent has good corrosion resistance.The reaction kettle 3, alkali resistance, glass lining laboratory for poor corrosion resistance of alkaline solution is acid solution.But put my factory glass lining sample in 1 n naoh solution corrosion, test temperature 80 ℃ time 48 h.4, operating temperature: glass coating equipment, heating and cooling should be slow.Our factory manufacture glass lining equipments use temperature of 20-200 ℃, heat-resistant modified 200 ℃ or higher.5, porcelain layer thickness: the thickness of porcelain glass equipment is 0.8 2.3 mm, the thickness of porcelain glass lining equipment accessories, 0.6 to 1.8 mm. 6, compression power: glass lining has good insulation, when the glass lining with 20 kv high frequency electric spark within the given thickness check the porcelain layer, the high frequency electric spark breakdown porcelain layer cannot.7, resistance to impact: layer of glass laboratory stress in reaction kettle is smaller, the better elasticity, the greater the hardness, bending the higher the compressive strength, the impact resistance is better.Our factory of glass layer within the specified thickness, with a diameter of 30 mm, weight of 112 g steel ball impact, it is 282 x 10-3 j impact energy (classy article index for 260 x 10-3 j).